Alloy 600 UNS N06600 Inconel 600® Tubing Nonmagnetic High Temperature

Yuhong Group Co.,Ltd
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment

Alloy 600 UNS N06600 Inconel 600® Tubing Nonmagnetic High Temperature

Brand Name : YUHONG SPECIAL STEEL

Model Number : ASME SB167 UNS NO 6600. UNS6600H

Certification : ABS, GL, DNV, NK, PED, AD2000, GOST9941-81, CCS, ISO 9001-2008

Place of Origin : China, USA, Korea, UE

MOQ : 100KGS

Price : negotiable

Payment Terms : T/T, L/C

Supply Ability : 1500 tons per month

Delivery Time : 10days->

Packaging Details : Ply-wooden Case /Iron Case/ Bundle with plastic Cap

Standard : B167, B163, B516, B517

Grade : Inconel600, NO6600, 2.4816

Size : OD:3MM TO 530MM ,WT:0.2MM TO 60MM, L:MAX 50M

PACKING : Ply-wooden Case or Iron Case

Contact Now

Alloy 600 UNS N06600 Inconel 600® Tubing Nonmagnetic High Temperature

Description

Alloy 600 is a nonmagnetic, nickel-based high temperature alloy possessing an excellent combination of high strength, hot and cold workability, and resistance to ordinary form of corrosion.
This alloy also displays good heat resistance and freedom from aging or stress corrosion throughout the annealed to heavily cold worked condition range.

Corrosion Resistance

The high chromium content of alloy 600 raises its oxidation resistance considerably above that of pure nickel, while its high nickel content provides good corrosion resistance under reducing conditions.
This alloy exhibits high levels of resistance to stress and salt water, exhaust gases, and most organic acids and compounds.

Heat Treatment

Alloy 600 is not an age hardening alloy; cold working is the only available means of hardening. Softening by annealing begins at about 1600°F (871°C), and is reasonably complete after 10 to 15 minutes of heating at 1800°F (982°C). Above this temperature, grain growth may be objectionable, although very brief heating at 1900°F will cause complete softening without undue grain growth. Since the rate of cooling has no effect on the softening, the material may be water quenched or air cooled.


Workability

Hot Working/Forging
Low sulfur reducing furnace atmospheres should be used in forging. Major hot working should be done between 2300/1850°F, while light working may be continued as low as 1600°F. No hot working should be attempted between 1600/1200°F due to lower ductility in that range.

Machinability
Alloy 600 is machinable in both the hot worked and annealed conditions. Because considerable heat is generated in machining this alloy, high-speed steel, cast nonferrous or cemented carbide tools should be used. The tools should be kept sharp.
Lathe turning speeds with high-speed and nonferrous tools are 35/45 sfm (0.18/0.23 m/s); speeds with cemented carbide tools are 100/175 sfm (0.51/0.89 m/s). (This data should be used as a guide for initial machine setup only. The figures used are averages. On certain work, the nature of the part may require adjustment of speeds and feeds.)
Sulfur-based oil should be used as a lubricant, but should be completely removed before the machined part is exposed to elevated temperatures, as in welding.

Cold Working
For higher properties, alloy 600 can be cold worked below 1200°F (649°C).

Welding
Alloy 600 can be joined by the usual welding , brazing, and soldering process.

Typical Mechanical Properties

Typical Mechanical Properties
Various forms and conditions

Form
and
Condition

Tensile Strength

0.2%
Yield Strength

% Elongation
in 2"

%
Reduction
of Area

Rockwell
Hardness

Rod and Bar
Cold-drawn
Annealed
As-drawn
Hot rolled
Annealed
As-rolled
Hot-finished
Strip
Annealed



80-100
105-150

80-100
85-120
80-120

80-100



552-689
724-1034

552-689
586-827
586-827

552-689



25-50
80-125

30-50
35-90
35-90

30-45



172-345
552-862

207-345
241-621
241-621

207-310



55-35
30-10

55-35
50-30
50-30

55-35



70-60
60-30

70-60
65-50
65-50

----



65-85B
90B-30C

65-85B
75-95B
75-95B

84B max.

Average Room Temperature Tensile Data

Form

Condition

Ultimate Tensile Strength,
Ksi (MPa)

Yield Strength at 0.2% offset,
Ksi (MPa)

Elongation in 2 in. (50.8mm)
or 4D, percent

Sheet
Plate
Bar/Billet
Sheet, Plate, Strip, Bar

Annealed
Annealed
Annealed
Annealed

98 (676)
95 (655)
95 (655)
80 (550)*

42 (290)
41 (283)
41 (283)
35 (240)*

40
45
45
30*

* - minimum

Sheet/Plate Round Bar Pipe Tube Fittings Forgings
ASME SB-168 AMS 5540 ASME SB-166 AMS 5665 ASME SB-167 ASME SB-829 ASME SB-517 ASME SB-775 ASME SB-163 ASME SB-516 ASME SB751 AMS 5580 ASME SB-366 ASME SB-564 AMS 5665

Applications

Some typical applications are:

  • Barge and tank truck liners
  • Carburizing atmospheres
  • Ethylene dichloride crackers
  • Furnace trays, mufflers, hangers
  • Gasoline stabilizer production
  • MgCl2 evaporates
  • Phenol condensers
  • Soap manufacture
  • Titanium dioxide
  • Vegetable and fatty acid vessels


Product Tags:

nickel alloy tube

      

hastelloy c tubing

      
 Alloy 600 UNS N06600 Inconel 600® Tubing Nonmagnetic High Temperature Manufactures

Alloy 600 UNS N06600 Inconel 600® Tubing Nonmagnetic High Temperature Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Yuhong Group Co.,Ltd
*Subject:
*Message:
Characters Remaining: (0/3000)